br>chrome-extension://efaidnbmnnnibpcajpcglclefindmkajbr>aLL THESE PLACES STILL MAKE GUNS BY HAND, FROM RAILWAY LINE STEEL TO BOILER ROOM PARTS.

Ja !- this is now a worry to me. Look, there ain't no way the action will be dumped, just not going to happen, but mmmnnn -Ya!Been reading on the...

Sorry to have to tell you, but those two labels are completely different.They are even different colors.You need an eye test, like the rest of us had ...

I'd be a bit iffy of that action now. The highest pressure I could find referenced for a 303 Brit proof load was 75k psi and early ones were in t...

Its there for like we spoke about, to create pressure for better burn characteristic's. There is not bullet to hold, hold and then break loose. T...

What bullet weight and what speed did you get? My QL calculation goes off the clock at 200K psi.****************************** ;D  ;D  ;D 17...

Momentum (speed x weight) plays a big role in penetration. I can remember a picture showing a 300gr (375HH) solid in an oak board. It penetrated 57 in...

Quick Load puts the pressure at 99000  PSI

They very different and yet so the same. 20240922_130608 by David Frank Allen, on Flickr20240922_130558 by David Frank Allen, on Flickr

Generally, it should be the case, but not always. Bullet speed, bullet construction,target medium etc play a role.***********************Ya - not inte...

What is also important is the ratio between case volume and caliber. A big case with a wide neck will require a faster powder, compared to the same ca...

Happy result. Ideally you want to start with a pure lead blank that is just a little over max possible bore dimension. It's also a good idea to l...

So if you look at it this way. All metal spheres have the same SD. If you drop a 1kg sphere or a 1g sphere from the same height onto a plank of wood, ...

just had a thought , I wonder what affect a dry slide, lack of lube would have on slide time and rearwards tug on pistol as it moves.If any that is .